Sponge titanium, also called porous titanium, is a kind of material produced through a specialized manufacturing process. The production process of sponge titanium involves the following steps:1. Raw Material Selection: High-quality titanium ore is selected as the raw material for the production of sponge titanium.2. Purification: Purification is required to remove any impurities from the raw material. The titanium ore is processed with the help of chlorine to remove impurities like iron and alu

The main differences between titanium radial forging tube and machining tube can be summarized as follows:



1. Material Efficiency: Radial forging produces tube-shaped parts without cutting off any metal, while machining requires cutting off excess materials, leading to higher material wastage.

The processing method of radial forging for titanium alloy bar is characterized by applying pressure to the metal from the radial direction. The titanium alloy bar is placed in the forging machine, and the rotating forging wheel applies pressure to the material, which causes the bar to deform along the radial direction. This process can improve the

The production process of Titanium Stub Ends GR2 3" S/10S MSS Type A ASTM B-363WPT2 involves several key steps. First, the raw material is carefully selected and tested for purity and quality. Then, the material is cut to the desired shape and size using CNC machines.

Introduction to the production process of 3 S/10S 90 deg pure titanium elbow Gr2 in accordance with ASTM B-363 standard, requiring sandblasting and acid washing of the surface without any defects such as cracks, scratches, or small pits. Finally, we will introduce the application fields and usage instructions of pure titanium elbows. To produce the 3 S/10S 90 deg pure titanium elbow Gr2 in accordance with ASTM B-363 standard, the following steps must be carried out:1. Raw material selection: Se

Ti 6Al 4V is a titanium alloy that is made up of 6% aluminum and 4% vanadium, and is known for its high strength-to-weight ratio and excellent corrosion resistance. AMS 4928 is a standard specification that outlines the requirements for the production of Ti 6Al 4V material, with a size of φ1.875"

Titanium alloy bike tubes Gr9 ASTM B338 size: OD25.4mm is a commonly used material in the bicycle industry due to its high strength, low density and excellent corrosion resistance. In order to ensure a high yield rate during bending, the proper heat treatment process must be applied. The recommended heat treatment process for Gr9 titanium alloy bike tubes is annealing. Annealing involves heating the material to a specific temperature and holding it there for a period of time. It helps to elimin

The production process of titanium foil with ASTM B265 standard, GR2 grade, and specifications of 0.127mm thickness and 304mm width starts with the selection of high-quality titanium sponge as the raw material. The titanium sponge is melted in a vacuum arc furnace or a plasma arc furnace to produce titanium ingots. The ingots are then hot rolled into plates of a certain thickness, followed by cold rolling to further reduce the thickness and improve the surface quality. After the desired thickn